CHEMICAL COMPOSITION ( IN PERCENTAGE ) |
||||||||||
Grade |
C (Max) |
Mn (Max) |
P (Max) |
S (Max) |
Si (Max) |
Cr |
Ni |
Mo |
Nitrogen (Max) |
Cu/ Others |
301 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
16.00 - 18.00 |
6.00 - 8.00 |
- |
0.10 |
- |
304 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
8.00- 10.50 |
- |
0.10 |
- |
304L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
8.00- 12.00 |
- |
0.10 |
- |
310S |
0.08 |
2.00 |
0.045 |
0.030 |
1.50 |
24.00- 26.00 |
19.00 - 22.00 |
- |
- |
- |
316 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 - 18.00 |
10.00 - 14.00 |
2.00 - 3.00 |
0.10 |
- |
316L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 - 18.00 |
10.00 - 14.00 |
2.00 - 3.00 |
0.10 |
- |
317 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
11.00 - 14.00 |
3.00 - 4.00 |
0.10 |
- |
317L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
11.00 - 15.00 |
3.00 - 4.00 |
0.10 |
- |
321 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 - 19.00 |
9.00 - 12.00 |
- |
0.10 |
Ti5 ( C + N ) Min or 0.70 max |
347 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 - 19.00 |
9.00 - 13.00 |
- |
- |
Cb= 10x ( C Min ) or 1.00 Max |
409 |
0.08 |
1.00 |
0.040 |
0.010 |
1.00 |
10.50 - 11.75 |
0.50 |
- |
- |
Ti= 6x (C+ N ) Min or 0.70 Max |
409M |
0.03 |
0.81.2 |
0.030 |
0.030 |
0.40.75 |
11.00- 12.00 |
1.5 max. |
- |
- |
Ti= 6x (C) Min or 0.70 Max |
410S |
0.08 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.60 |
- |
- |
- |
410 |
0.15 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.75 |
- |
- |
- |
420 |
0.35 |
0.50 |
0.035 |
0.015 |
0.50 |
12.00 - 13.00 |
0.20.3 |
- |
- |
- |
430 |
0.12 |
1.00 |
0.040 |
0.030 |
1.00 |
16.00 - 18.00 |
0.75 |
- |
- |
- |
JSL AUS |
0.08 |
7.08.0 |
0.070 |
0.030 |
0.75 |
15.50 - 16.50 |
4.25 - 4.75 |
- |
- |
0.9 - 1.10 |
JS- 203 |
0.08 |
9.2510.25 |
0.070 |
0.030 |
0.75 |
14.25 - 15.25 |
2.25 - 2.75 |
- |
- |
1.60- 2.0 |
301M |
0.10 |
4.55.5 |
0.060 |
0.030 |
0.75 |
14.50 - 15.50 |
6.0 - 7.0 |
- |
- |
1.70- 1.90 |
* Thickness of 1.27mm & below will have elongation of 20% min. |
||||||||||